Heat Fluorinated Ethylene-propylene (FEP) Shrinkable Sleeve
FEP heat-shrinkable sleeve is made from FEP resin and is prepared by the technology of extrusion and blowing. FEP heat-shrinkable sleeve has a high UV transmission, UV resistance and good electric property. The shrinkage temperature is from 130℃～200℃. The shrinkage rate is about 30%. Another major advantage of FEP heat-shrinkable sleeve is being heat-sealed or welded to itself. So, FEP heat-shrinkable sleeve can be used as cable jackets, non-stick rollers, sensor probe covers, hose protection, electrical terminal insulation etc. It conforms to the enterprise standard of Q/GHAD 59-2006.
Main Properties
|
Item |
Value |
|
Tensile Strength MPa ≥ |
20 |
|
Elongation @ Break % ≥ |
150 |
|
Dielectric Strength
(KV/mm) ≥ |
Wall Thickness after shrinkage≤0.3mm |
10 |
|
0.3mm＜Wall Thickness after shrinkage≤0.4mm |
11 |
|
Wall Thickness after shrinkage＞0.4mm |
12 |
Specification
|
Code |
I.D. |
Wall Thickness after shrinkage |
Continues Length |
|
Min.
(Before Shrinkage) |
Max.
(After Shrinkage) |
Wall Thickness & Tolerance |
|
FEP-G-S-1 |
6.5 |
5 |
0.20±0.08
0.25±0.08
0.30±0.08
0.40±0.08
0.5±0.10
0.6±0.15
0.7±0.15 |
≥500 |
|
FEP-G-S-2 |
8 |
6 |
≥500 |
|
FEP-G-S-3 |
9 |
7 |
≥500 |
|
FEP-G-S-4 |
10 |
8 |
≥500 |
|
FEP-G-S-5 |
12 |
9 |
≥500 |
|
FEP-G-S-6 |
14 |
10.5 |
≥500 |
|
FEP-G-S-7 |
15 |
11 |
≥500 |
|
FEP-G-S-8 |
16 |
12 |
≥500 |
|
FEP-G-S-9 |
18 |
13.5 |
≥500 |
|
FEP-G-S-10 |
22 |
16 |
≥500 |
|
FEP-G-S-11 |
24 |
18 |
≥500 |
|
FEP-G-S-12 |
26 |
20 |
≥500 |
|
FEP-G-S-13 |
29 |
22 |
≥500 |
|
FEP-G-S-14 |
32 |
25 |
≥500 |
|
FEP-G-S-15 |
38 |
30 |
≥500 |
|
FEP-G-S-16 |
41 |
32 |
≥500 |
|
FEP-G-S-17 |
45 |
35 |
≥500 |
|
FEP-G-S-18 |
50 |
38 |
≥500 |
|
FEP-G-S-19 |
52 |
40 |
≥500 |
|
FEP-G-S-20 |
60 |
45 |
≥500 |
|
FEP-G-S-21 |
72 |
55 |
≥500 |
|
FEP-G-S-22 |
90 |
70 |
≥500 |
|
FEP-G-S-23 |
115 |
90 |
≥500 |
|
FEP-G-S-24 |
130 |
110 |
≥500 |
|
FEP-G-S-25 |
140 |
120 |
≥500 |
|
Note: Customer’s request negotiable |